A335 PIPE SPECIFICATIONS

December 24, 2018

A335 PIPE SPECIFICATIONS

A/SA335
NPS 1/4″ – 24″
Schedules 40 through 160, STD, XH and XXH

Scope

This specification covers nominal wall and minimum wall seamless ferritic alloy-Steel Pipe intended for high-temperature service. ASTM A335 pipe ordered to this specification shall be suitable for fusion welding, bending, flanging (vanstoning), and similar forming operations.


Material & Manufacture

Pipe may be either hot finished or cold drawn with the finishing heat treatment noted below.


Heat Treatment Requirements

P5, P9, P11, and P22    
Grade Heat Treatment Type Normalizing Temperature Range F [C] Subcritical Annealing or Tempering
Temperature Range F [C]
P5 (b,c) Full or Isothermal Anneal
Normalize and Temper ***** 1250 [675]
Subcritical Anneal (P5c only) ***** 1325 – 1375 [715 – 745]
P9 Full or Isothermal Anneal
Normalize and Temper ***** 1250 [675]
P11 Full or Isothermal Anneal
Normalize and Temper ***** 1200 [650]
P22 Full or Isothermal Anneal
Normalize and Temper ***** 1250 [675]
P91 Normalize and Temper 1900-1975 [1040 – 1080] 1350-1470 [730 – 800]
Quench and Temper 1900-1975 [1040 – 1080] 1350-1470 [730 – 800]

Chemical Requirements

Grade P-5 P-9 P-11 P-22 P-91 P-91 shall also include the following:
Element UNS Designation K41545 S50400 K11597 K21590 K91560
Carbon 0.15 max 0.15 max 0.05 – 0.15 0.05 – 0.15 0.08 – 0.12 V at 0.18 – 0.25
Manganese 0.30 – 0.60 0.30 – 0.60 0.30 – 0.60 0.30 – 0.60 0.30 – 0.60 N at 0.030 – 0.070
Phosphorous, max 0.025 0.025 0.025 0.025 0.020 Ni at 0.40 max
Sulfur, max 0.025 0.025 0.025 0.025 0.010 Al at 0.02 max
Silicon 0.50 max 0.25 – 1.00 0.50 – 1.00 0.50 max 0.20 -0.50 Cb at 0.06 – 0.10
Chromium 4.00 – 6.00 8.00 – 10.00 1.00 – 1.50 1.90 – 2.60 8.00 – 9.50 Ti at 0.01 max
Molybdenum 0.45 -0.65 0.90 – 1.10 0.44 – 0.65 0.87 – 1.13 0.85 – 1.05 Zr at 0.01 max

Tensile Requirements

Seamless    
    P-5 P-9 P-11 P-22 P-91 P91 shall not have a hardness not exceeding 250 HB/265 HV [25HRC].
Tensile Strength, min., psi
ksi 60 60 60 60 85
MPa 415 415 415 415 585
Yield Strength, min., psi
ksi 30 30 30 30 60
MPa 205 205 205 205 415

Permissible Variation in Wall Thickness

NPS [DN] Designator Tolerance, % from Specified
Over Under
1/8 to 2 1/2 [6 to 65] incl., all t/D ratios 20.0% 12.5%
Above 2 1/2 [65], t/D < or = 5% 22.5% 12.5%
Above 2 1/2 [65], t/D > 5% 15.0% 12.5%
(t = Specified Wall Thickness; D = Specified Outside Diameter)

Elongation Requirements

Calculated Minimum Elongation Values
Elongation in 2 in. or 50 mm, min %
Wall Thickness P5, P9, P11, P22   P91
in. mm Longitudinal Transverse   Longitudinal
5/16 (0.312) 8 30 20 20
9/32 (0.281) 7.2 28 19 19
1/4 (0.250) 6.4 27 18 18
7/32 (0.219) 5.6 26 17
3/16 (0.188) 4.8 24 16
5/32 (0.156) 4 22 15
7/8 (0.125) 3.2 21 14
3/32 (0.094) 2.4 20 13
1/18 (0.062) 1.6 18 12

Permissible Variations in Outside Diameter

Outside Diameter at any point shall not vary from standard specified more than:

NPS [DN] Designator Over Under
in. mm in. mm
1/8 to 1 1/2 [6 to 40], incl. 1/64 (0.015) 0.40 1/64 (0.015) 0.40
Over 1 1/2 to 4 [40 to 100], incl. 1/32 (0.031) 0.79 1/32 (0.031) 0.79
Over 4 to 8 [100 to 200], incl. 1/16 (0.062) 1.59 1/32 (0.031) 0.79
Over 8 to 12 [200 to 300], incl. 3/32 (0.093) 2.38 1/32 (0.031) 0.79
Over 12 [300] +/- 1% of the specified outside diameter

Mechanical Tests Specified

Transverse or Longitudinal Tension Test and Flattening Test, Hardness Test, or Bend Test
For material heat treated in a batch-type furnace, tests shall be made on 5% of the pipe from each treated lot. For small lots, at least one pipe shall be tested.
For material heat treated by the continuous process, tests shall be made on a sufficient number of pipe to constitute 5% of the lot, but in no case less than 2 pipe.
Notes for Hardness Test: P91 shall not have a hardness not exceeding 250 HB/265 HV [25HRC].
Notes for Bend Test: For pipe whose diameter exceeds NPS 25 and whose diameter to wall thickness ratio is 7.0 or less shall be subjected to the bend test instead of the flattening test.
Other pipe whose diameter equals or exceeds NPS 10 may be given the bend test in place of the flattening test subject to the approval of the purchaser.
The bend test specimens shall be bent at room temperature through 180 without cracking on the outside of the bent portion.
The inside diameter of the bend shall be 1 inch [25 mm].
Hydrostatic Test Each length of pipe shall be Hydro tested, at option of manufacture, nondestructive electric testing can be used.

The above is the A335 PIPE SPECIFICATIONS we have listed for you. You can submit the following form to obtain more industry information we provide for you.

You can visit our website or contact us, and we will provide the latest consultation and solutions

Share to:

Send Inquiry

Home> Industry Information> A335 PIPE SPECIFICATIONS
Communicate with Supplier?Supplier
luffy Ms. luffy
What can I do for you?
Contact Supplier