ASTM A420 WPL6 pipe Elbow after complete quality and performance measure inspection. These are widely appreciated for excellent quality, corrosion abrasion and high tensile strength with long life service.. WPL6 is a normalized grade of carbon steel that has been Charpy Impact tested at -50 degree F for use in low temperature service. See Also ASTM A333 Grades 1 and 6 (for pipe) and A350 LF2 for Steel Flange .
ASTM A420 WPL6 Elbow after complete quality and performance measure inspection. These are widely appreciated for excellent quality, corrosion abrasion and high tensile strength with long life service.
Materials shall consist of forgings, bars, plates, seamless or fusion welded tubular products with filler metal added, and shall be produced by open-hearth, basic-oxygen, or electric-furnace process. Forging or forming operations shall be performed by one or a combination of two or more of the following procedures: hammering, pressing, piercing, extruding, upsetting, working, bending, fusion-welding, or machining. All welding shall be completed prior to the austenitizing heat treatment, which shall be executed in the normalized, normalized and tempered, annealed, or quenched and tempered conditions. Steel specimens shall conform to required values of chemical composition, tensile strength, yield strength, elongation, wall thickness, and Charpy V-notch impact value. All fusion-welded butt joints shall undergo radiographic examination, while hydrost
atic testing of fittings is not required in this specification. Repair welding shall be permissible for parts made to dimensional standards.
Scope of ASTM A420
1.1 This specification covers wrought carbon steel and alloy steel fittings of seamless and welded construction, covered by the latest revision of Asme B16.9 , ASME B16.11, MSS SP-79, MSS SP-83, MSS SP-95, and MSS SP-97. Fittings differing from these ASME and MSS standards shall be furnished in accordance with Supplementary Requirement S58 of Specification A960/A960M. These fittings are for use in pressure piping and pressure vessel service at low temperatures.
1.2 Optional supplementary requirements are provided for fittings where a greater degree of examination is desired. When desired, one or more of these supplementary requirements shall be specified in the order.
1.3 This specification is expressed in both inch-pound units and in SI units. However, unless the order specifies the applicable [M" specification designation (SI units), the material shall be furnished to inch-pound units.
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
Chemical Composition (%) of ASTM A420
| Grade | C | Mn | P | S | Si |
| WPL6(1)(2) | 0.3 | 0.60-1.35 | 0.035 | 0.04 | 0.15-0.30 |
| WPL9 | 0.2 | 0.40-1.06 | 0.03 | 0.03 | - |
| Grade | Ni | Cu | Cr | Mo | V | Nb |
| WPL6(1)(2) | 0.4 | 0.4 | 0.3 | 0.12 | 0.08 | 0.02 |
| WPL9 | 1.60-2.24 | 0.75-1.25 | - | - | - | - |
GENERAL NOTE:
All values are maximum unless otherwise indicated.
NOTES:
(1) For each reduction of 0.01% C below 0.30%, an increase of 0.05% Mn above 1.06% will be permitted, up to a maximum of 1.35%.
(2) Fittings made from forgings may have 1.35% max Mn.
Mechanical properties of ASTM A420
| Tensile Requirements | WPL6 | WPL9 |
Tensile Strength
min, ksi [MPa] | 60-85[415-585] | 63-88[435-610] |
Yield Strength
min, ksi [MPa] | 35[240] | 46[315] |
Where the wall thickness lies between two values above, the min elongation value is determined by the following equations:
WPL6,WPL9
Longitudinal E=48t+15.00,E=48t+13.00
Transverse E=32t+6.50,E=32t+8.00
E = elongation in 2in [50mm], %
t = actual thickness of specimen, in [mm]
Impact Test Properties
Since these pipe fittings are primarily used for low-temperature service, the properties of charpy V-notch impact test must be considered.
Charpy Impact Requirements for WPL6, WPL9, and WPL3
| |
| Size of Specimen | A* | B* |
| mm | ft·lbf | J | ft·lbf | J |
| 10 by 10.0 | 13 | 17.6 | 10 | 13.6 |
| 10 by 7.5 | 10 | 13.6 | 8 | 10.8 |
| 10 by 5.0 | 7 | 9.5 | 5 | 7.0 |
| 10 by 2.5 | 4 | 5.4 | 3 | 4.1 |
A*Charpy V-Notch Impact Value Required for Acceptance (Average of Three Specimens)
B*Minimum Charpy V-Notch Impact Value Without Requiring Retest (One Specimen Only of a Set)Charpy Impact Requirements for WPL8
| |
| Size of Specimen | A* | B* |
| mm | ft·lbf | J | ft·lbf | J |
| 10 by 10.0 | 25.0 | 33.9 | 20.0 | 27.1 |
| 10 by 7.5 | 21.0 | 28.5 | 17.0 | 23.1 |
| 10 by 5.0 | 17.0 | 23.1 | 14.0 | 19.0 |
| 10 by 2.5 | 8.0 | 10.8 | 6.0 | 8.1 |
A*Charpy V-Notch Impact Value Required for Acceptance (Average of Three Specimens)
B*Minimum Charpy V-Notch Impact Value Without Requiring Retest (One Specimen Only of a Set)
Impact Test Temperature
| |
| Grade | °F [°C] |
| WPL6 | −50 [−45] |
| WPL9 | −100 [−75] |
| WPL3 | −150 [−100] |
| WPL8 | −320 [−195] |
The raw material for these fittings shall be fully killed steel, consisting of forgings, bars, plates, sheet, and seamless or fusion welded tubular products(pipes, tubes, or cylinders).
Con Reducer 10″x6″(wt. 1.625″x1.062″),
ASTM A420 WPL6 Pipe Fitting
The steels shall be made using recognized melting practices necessary to produce steels that shall meet the impact requirements of ASTM A420. The ASTM A420 fittings may be made by forging or forming operations including hammering, pressing, piercing, extruding, upsetting, working, bending, fusion-welding, or machining, or by a combination of two or more of these operations. The forming procedure shall be so applied that it will not produce injurious defects in the fittings. All the fittings shall be furnished free of welding repair. The welded joints of the fittings shall be finished in accordance with the requirements of Paragraph UW-35 (a) of Section VIII, Division 1 of ASME Boiler and Pressure Vessel Code.
Product & Standards
| Standards | Product |
| ASME B16.9 | Factory-Made Wrought Steel Butt Welding Threaded |
| ASME B16.11 | Forged Steel Fittings, Socked Welding Threaded |
| ASME Section VIII Division 1 | Pressure Vessels |
| MSS SP-25 | Standard Marking System for Valves, Fittings, Flanges, and Unions |
| MSS SP-79 | Socket Welding Reducer Inserts |
| MSS SP-83 | Steel Pipe Unions, Socket-Welding and Threaded |
| MSS SP-95 | Swage(d) Nipples and Bull Plugs |
| MSS SP-97 | Integrally Reinforced Forged Branch Outlet Fittings-Socket Welding, Threaded and Buttwelding Ends
|
A420 Wpl6 Carbon Steel Pipe Fitting
A403 304/304L Elbow ,316/316L Pipe Fitting
Small size Reducing Elbow
A860 Wphy52 Elbow,A860Wphy65 Elbow
Stainless Steel Forging Elbow
Galvanized Elbows Fittings
Weld Threaded Socket Fittings
Pipe fittings manufactured to ASTM A420 shall take the following tests or inspections: dimensional inspection, visual examination, hydrostatic test(when required), chemical analysis, tensile test, impact test, radiographic test(RT).